Click image to view full size image
Zamak ingot, Zn ingot
Min. Order: 1metric ton
Supply ability: 4000 metric ton
Shape: Ingots about 12 kg
Zinc ingot, Zamak ingot
Zinc alloy "zamak 5" turkish origin according to the European origin EN1774 for the egyption market and international markets
Analysis:
Al%: 3.8-4.2%
Mg%: 0.035-0.06%
Cu%: 0.7-1.1%
Fe%: 0.02% max
Pb%: 0.003% max
Sn%: 0.001% max
Ni% 0.001% max
Cd%: 0.003% max
Zamak 5 propertiesPropertyMetric valueEnglish valueMechanical propertiesPhysical properties
USAGE:
1. Mainly used for die-casting alloy battery industry
2. Widely used in Painting/ Printing/Dyeing/pharmaceutical/rubber industry etc.
3. Chemical industries, zinc and other metal alloy plating coating industry
4. In zinc plating, manufacture of brass, maganese bronze, galvanized iron, dry battery; As catalyst and reducing agent.
Min. Order: 1metric ton
Supply ability: 4000 metric ton
Shape: Ingots about 12 kg
Zinc ingot, Zamak ingot
Zinc alloy "zamak 5" turkish origin according to the European origin EN1774 for the egyption market and international markets
Analysis:
Al%: 3.8-4.2%
Mg%: 0.035-0.06%
Cu%: 0.7-1.1%
Fe%: 0.02% max
Pb%: 0.003% max
Sn%: 0.001% max
Ni% 0.001% max
Cd%: 0.003% max
Zamak 5 propertiesPropertyMetric valueEnglish valueMechanical propertiesPhysical properties
USAGE:
1. Mainly used for die-casting alloy battery industry
2. Widely used in Painting/ Printing/Dyeing/pharmaceutical/rubber industry etc.
3. Chemical industries, zinc and other metal alloy plating coating industry
4. In zinc plating, manufacture of brass, maganese bronze, galvanized iron, dry battery; As catalyst and reducing agent.
|
ltimate tensile strength |
331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 |
|